GENERAL CATALOGUE


SURFACE TREATMENT PRODUCTS

BY

KIZAI


AGENTS

TAIWAN Nabelin CO.,LTD.
ETERNITY ENTERPRISE(tiwan),LTD.
10th Fl. No.201,Sec.3 Nanking East Rd.,
TAIPEI, TAIWAN, R.O.C..
TEL : 886-2-2545-0520 FAX : 886-2-2545-0524
HONG KONG
SOUTH PART
OF CHINA
CHEMTECH ELECTROPLATING CHEMICALS LTD.
6/F., Blook A-B, Richwealth Industrial Bldg., 77-87,
Wang Lung Street Tsuen Wan, N.T. Hong Kong
TEL : 852-24073303 FAX : 852-24089867
CENTER PART
OF CHINA
SHANGHAI RICA ENVIRONMENTAL
No.199, Zhang Wen Miao Road, Fenngxian country
Shanghai, CHINA
TEL : 86-21-33659252 FAX : 86-21-33659251
NORTH PART
OF CHINA
YIN XIANG(TIANJIN) INTERNATIONAL TRADE CO.,LTD
Ming Du Building The Fourth Floor, La Sa Street,
NO.48 He Ping District, TIANJIN. CHINA
TEL : 86-22-27814725 FAX : 86-22-27821531
MALAYSIA
SHINGAPORE
RICA MARKETING SDN. BHD.
.NO.7 Jalan Taming Tiga, Taman Taming Jaya,
(Taming Industrial Park) Off Jalan Balakong 43300
Selangor, MALAYSIA
TEL : 60-3-89614950 FAX : 60-3-89613954
KOREA SHINDONG CHEMICAL CO.,LTD.
No.1204, E&C DREAM TOWER Yangpyeong-dong
3ka, Youngdeungpo-gu Seoul, 150-103, KOREA
TEL : 82-2-2631-7591 FAX : 82-2-2631-7593
INDONESIA PT PINTU MAS MULIA KIMIA
JalanTanahAbang VNo.5-7, Jakarta 10160 INDONESIA
TEL : 62-21-3440862 FAX : 62-21-3440856,3440896
THAILAND YA THAI CHEMICAL CO.,LTD.
78/9 Moo 5 Takam Bangpakong
Chachoengsao 24130, THAILAND
TEL : 66-38-574-400 FAX : 66-38-573-700
INDIA PROTOCHEM INDUSTRIES PVT.LTD.
2 7 Unique Industrial Estate,Dr.R.P.Road,Mulund(W)
Mumbai-400080,INDIA
TEL : 91-22-25683279 FAX : 91-22-25680013


" Mar. 2013 "

KIZAI CORPORATION HEAD OFFICE : 9-10 Nihonbashi Kodenma-cho, Chuo-ku, Tokyo.
TEL : 81-3-3662-8871 FAX : 81-3-3661-8636
E-Mail : tokyo@kizai-chem.co.jp
Home Page : http://www.kizai-chem.co.jp/


BUFFERING COMPOUND REMOVER BACK

MAXCLEEN BG-600

Polishing Residue Remover for almost metals such as for
steel,copper,brass,aluminum and other non ferrous metals. (chelating agent)
Operating condition - 20-50ml/L, 60-90ーC

CLEANING AGENT BACK

IMMERSION TYPE

MAXCLEEN BGF-220H

For ferrous metals use without chelating Agent but extremely powerful cleaner so even
used under severe condition show satisfactory results. (Non chelating agent)
Operating condition - 40-60g/l, temperature 50-80ーC

MAXCLEEN BGF-220S

For ferrous metals use against oily composition and being
non tarnishing on brass. (Non chelating agent)

Operating Condition - 40-60g/l, temperature 60-80ーC

MAXCLEEN BG-20

For non ferrous metals use, a non Chelating Agent powerful cleaner
but do not affect base metal.
Operating condition - 30-80g/l, temperature 60-80ーC

MAXCLEEN NG-30

A neutral (pH 7.7) cleaner without Chelating Agent and phosphate for non ferrous metals
(including aluminum)use. Also, will not erode painted surface of most metals and
with strong emulsion power , it is a product showing excellent cleaning results.
Operating condition - 30-50g/l, temperature 40-60ーC

MAXCLEEN FL-828

Cleaning agent with Non Chelating Agent for copper alloy, aluminum die cast
and other non ferrous metals, Specially effective for Electronics condenser chips,
chip resistance such as ceramics materials.

Operating Condition - 30-100ml/l, 30-50ーC

TEION CLEANER BG-50

Low temperature degreasing agent for copper, copper alloy and zinc die cast.

IMMERSION/SPRAY & ELECTROLYTIC TYPE

TEION CLEANER BGF-510

Low temperature degreasing agent for steel base surface..

MAXCLEEN BGF-502B

Contain Chelating Agent , a extremely powerful cleaning and buffing compound
removing type cleaner. Can be used from electro to immersion or vice versa
so rinsing processingtime can be rationalized to great extent.

Operating condition - 40-80g/l, 70-90ーC(immersion), 80-100g/l, 40-80ーC(electro)

MAXCLEEN BGF-505

A powerful cleaning and buffing compound removing type cleaner with chelating agent for
ferrous metals use. Non ion type surfactant used so no foaming. Also, do not
contain Silicate and can be used for spray cleaning with excellent results.

Operating condition - 40-80g/l, 70-90ーC(immersion), 20-50g/l, 40-90ーC(spray).

MAXCLEEN BGF-507

Same as BGF-507 with chelating agent and without Silicate but more powerful cleaner
in removing buffing compound and grease. Also, oil separating type so very economical.
Operating condition - 40-60g/l, 70-90ーC

ELECTRO TYPE

TAF LIQUID

A Non cyanide electro cleaner with Chelating Agent but have same superb power as electro
cleaner with cyanide. Also, activate nickel plated surface for replating and have strong
rust removing power. Also,the maximum permissible range of metal impurities is very
wide and moreover long solution life so very economical.

Operating condition - TAF LIQUID 50ml/l, Caustic Soda 50g/l, R.T.-50ーC, 3-10 a/dm2
parts to be cathodic.

TAF SHINE #3010

For ferrous metals use, a non Chelating Agent and non Silicate type electro cleaning agent
so waste water treatment very simple.

Operating condition - #3010/#3030 100g/l, 40-70ーC, 5-10A/dm2, P.r. or parts to be anodic.

TAFCLEEN SD

for ferrous metals use, specially to remove rust, smut and grease from iron
non cyanide, alkaline type.

Operating condition - TAFCLEEN SD 50-100g/l, Caustic soda 50-100g/l
Liquid temperature 60ーC, 5-10A/dm2, PR or Parts to be anodic(+)

TAF CLEEN-EX

For ferrous metals use, a non Cyanide electro cleaner with Chelating Agent used at full
strength so easy to handle and very economical chemical to use.

Operating condition -50-120g/l,room temperature-50ーC, 5-10A/dm2, P.R. or parts to be anodic.

MAX CLEEN BG-200

For non ferrous metals.Do not contain Chelating Agent but have extremely strong cleaning
and buffing compound removing power and do not affect base material.

Operating condition - 20-40g/l, 50-60ーC,6-7A/dm2, parts to be cathodic.

MAX CLEEN BG-3200

For non ferrous metals, A electro cleaner without Chelating Agent and Silicate most
suited for simple waste water treatment.

Operating condition - 30-60g/l, 40-60ーC, 3-10A/dm2, parts to be anodic or cathodic.

LIGHT-UP #202

Most popular electro cleaner with Chelating Agent for use with cyanide.

Operating condition - LIGHT-UP #202 30-50ml/l, Caustic Soda 60-100g/l, Sodium cyanide
60-100g/l, P.R. or parts to be cathodic.

SMUT SCALE AND REMOVER AGENT BACK

KOKEISAN-A

A safe acid cleaner without Chelating Agent, Fluoride and Surfactant for use before plating
to remove oxidized film on metal surface then activate to improve the adhesion of plating
in powdered form so no danger in handling and storage. Also, being different from standard
acid, have big pH buffer action so pH remains stable even used for long period of time and
operating condition stabilized.

Operating condition - 50-100g/l, room temperature.

KOKEISAN-B

Special character and application are as KOKEISAN-A but contain Fluoride so more
powerful. Especially suited for parts with soldered portion.

Operating condition -50-100g/l, room temperature-50ーC.

NEW KOKEISAN-EX

In Fluoride powdered form without Chelating Agent and Surfactant for adding to acid solution.
Used for removing heavy scale and flux from soldered and welded parts. Also can be used
together with nitric acid to activate silicate-aluminum alloy

Operating condition - Depending on acid solution 10-100g/l, room temperature -50ーC

KOKEISAN-RP

Do not contain Chelating Agent and Fluoride. Used for activation on replating of ferrous
metals, copper and nickel with excellent plating adhesion results.

Operating condition - 150-200g/l, room temperature-60ーC

SANDENKAI EX

A acid electro cleaner without Chelating Agent. Used for removing scale, smut and for
degreasing at short period of time. Also, simple waste water disposal.

Operating condition - SANDENKAI EX 100ml/l, Sulfuric acid 100ml/l, room temperature-40ーC.
cathodic.

MAXCLEEN ARF-404

Do not contain Chelating Agent. Used as immersion or electro cleaner to remove rust,
scale and smut from welded or treated portion of steel.

Operating condition - 1 part ARF-404, 2 part water , 40-70ーC.

MAXCLEEN BR-55

Only dipping the materials, within a short time rust or smut could be removed
for any of steel products. As this is alkaline type, removing smoothly.

Operating condition - 100g/l, 50-70ーC., 5-25 min.(standard 10min)
cathodic.

ADDITIVE FOR ACID AND ALKALI BACK

MAXCLEEN BEG-306

Additive surfactant with strong inhibitor to acid for cleaning and removing rust only without
affecting the base material.

Operating condition - 3-7% (hydrochloric acid) room temperature 3-7% (sulfuric acid)
room temperature -40ーC.

MAXCLEEN NEG-304 / 304 BL

For use with hydrochloric acid to remove rust or scale from metal at short period of time.
Contain inhibitor so prevent smut and at the sametime give effective degreasing.
Moreover, prevent mist forming. Widely used especially for pretreatment of Zinc plating.

Operating condition -3-7% (hydrochloric acid), room temperature.

DECORATIVE ALLOY METAL PLATING BACK

STANALLOY PROCESS

・Selection from 6 different colors ;
・Stanalloy Rose-White Tin - Tin -nickel alloy plating and color tone very close to stainlesss.
・Stanalloy Chrome Color - Tin-cobalt alloy plating and color tone very close to chrome plating.
・Stanalloy SPECULA - Copper-tin alloy plating with beautiful color tone of bright silver white color.
・Stanalloy Neo-Black - Tin-nickel alloy plating and color tone very close to black nickel.
・Stanalloy Pearl Blue - Tin-cobalt alloy plating which can obtain elegant color tone of deep
            black bluish color from pale black bluish color just by changing the concentration.

・Stanalloy Rose-Brown - Tin-nickel alloy plating and color tone is light brown blackish color.
 Easy to adjust color from white to black. simple solution control with good solderability and
 can be used for both rack and barrel plating.

KINBRONZ

Developed by KIZAI, a new bronz type gold color plating. The color is very elegant. Easy to
obtain color from 24K gold color to yellow color. Compared with brass plating the special
characteristic of KINBRONZ is no stain after plating. Can be used in place of gold plating
or undercoat for gold plating.

STANALLOY NEO-BLACK

This is the new exciting GUN METAL BLACK color. The corrosion and discoloration resistance
is far more superior than the black nickel plating. Operating is simple and have good
solution stability.

PLATING CHEMICALS FOR ELECTRONIC PARTS BACK

KARBON HANDA CF

A completely new non-fluorine ion and non chlorine ion neutral solder plating solution
(Pat. Pend.) developed by KIZAI. Compared to fluoride bath, the new special characteristics
Best for barrel plating of electronic parts.

PYROBAS-TIN - PYROBAS-TIN is a neutral tin plating method by pyrophosphoric acid bath. Can obtain good plating film by simple bath control with excellent solution stability and throwing power. Also, have good properties of fine grain and solderbility.

THP NEO Process - This process is chemical plating of through hole on printed circuit board. Fine grain chemical copper plating with excellent adhesion for through hole parts and copper parts.

EL-ACTAR-1 - Powerful metal activation agent. Uniform activation and can give good adhesion. Also, dissolving of metal is very little so long life and moreover, can be used at room temperature so very economical.

HEART BONDER SERIES                    See Page

NEW PRODUCT HEART BONDER SN22 is also non-fluorine ion and non chlorine ion solder plating
solution. It is not only excellent solderability but have good throwing power and solution
stability. It is also, easy to control solution and can be used for barrel plating
specially for electronic chips condensers, chips resistance.

HIGH CORROSION RESISTANT NICKEL PLATING PROCESS

EVANI PROCESS

A superb nickel alloy plating process to give excellent resistance to any material. Compared
with double or triple nickel plating , much savings can be made on nickel and obtain higher
productivity. The plating solution of EVANI PROCESS is easy to maintain control so very
economical.

HARD NICKEL PLATING PROCESS

NIPHOLLOY PROCESS

A simple electrolytic phosphorous-nickel alloy plating process having superior wear -resistance,
excellent hardness and high corrosion resistance. Compared to electroless nickel plating,
cost of chemical is much lower and moreover, larger production volume by simple operating
condition. Also, compared with to hard chrome, due to higher current efficiency and greater
throwing power, auxiliary anode is not necessary and shorter plating time.

HIGH CORROSION RESISTANT STRIKE FOR ZINC PLATING

STANOZIN STRIKE

This strike bath was developed especially for undercoat of zinc plating and plating deposit
is tin-zinc alloy. Compared to zinc plating or cyanide copper strike, the plating covering
power is more superior and with just 1 micron give excellent salt spray resistance.

CHEMICALS FOR PLASTIC PLATING BACK

CHEMIPLATE PROCESS

For electroless copper plating on plastics with good adhesion. Depending on pretreatment
process, ABS, P.P. and other plastics can be plated. This process has 2 types of electroless
copper plating solution as follows;
1) Cp-Cu 305 temperature 23-28ーC

NYCO PLATE PROCESS

For electroless nickel plating on plastics. Like CHEMIPLATE PROCESS has good adhesion
and there are 2 types of electroless nickel plating solution as follows:
1) NYCO-SP temperature 30-50ーC

ENGINEERING PLASTICS PLATING

KIZAI'S EP SERIES WITH EXCELLENT ADHESION FOR ENGINEERING PLASTIC PLATING

EP-GL Process For Polyphenylene Ether/Polyamide alloy
EP-PA Process For 6 Nylon
EP-LE Process For 66 Nylon
EP-POM Process For Polyacetal
EP-NL Process For Modified Poly Phenylene Oxide(NORYL)
EP-V Process For Liquid Crystal Polymer
EP-PP Process For Polypropylene
EP-PC Process For Polycarbonate & Polycarbonate/ABS Alloy
EP-PBT Process For Polyethylene Terephthalate
EP-PS Process For Polysulfone
EP-UD Process For Polyether Imide
EP-PES Process For Polyether Sulphone
EP-EPO Process For Epoxy resin

ELECTROLESS NICKEL PLATING ON CERAMICS BACK

NYCO-CER PROCESS

A electroless nickel plating process for ceramic circuit board. Also, give good solderbility
and low coefficient of friction on ceramic surface.

ELECTROLESS NICKEL PLATING ON METALS

NYCO-ME SERIES

NYCO-ME BR For brightner use
NYCO-ME AR For automatic replenishing
NYCO-ME-SB For super bright
NYCO-ME KU For hiigh corrosion resistance and good solderbility
NYCO-ME V For long life
NYCO-ME N For neutralizer


EN PLATE PROCESS SERIES

EN PLATE PROCESS EN-DL - Long life usage.

EN PLATE PROCESS EN-AL - High tolerance of zinc in electroless nickel plating is
used after on SUPER ZINCATE PROCESS ( aluminum alloy displacement solution )
so can use for long hours..

PLATING STRIPPER AGENT BACK

NEW RIP MASTER #1219

Most Widely used Stripper Agent in Japan. Used with sodium Cyanide to strip copper and
nickel on steel. Also, can be used with Sulfuric Acid to strip nickel on copper or brass.

Operating condition - for steel NEW RIP MASTER #1219 50g/l , Sodium Cyanide 100g/l, R.T.-45ーC.
for copper or brass NEW RIP MASTER #1219 100g/l, Sulfuric Acid 100ml/l, ST Addtive 10ml/l,
50-65ーC.

RIP MASTER PLUS / RIP MASTER #3000

Used by mixing RIP MASTER PLUS(liquid) and RIP MASTER #3000(powder) without Cyanide to
strip nickel on steel.

Operating condition - RIP MASTER PLUS 180-200ml/l, RIP MASTER #3000 40g/l, 40-50ーC.

RIP MASTER NRP-10

This chemical specially developed by Kizai to strip copper, nickel and electroless nickel on
plastics or stainless steel. Stripping time is very fast and life of chemical is long so
very economical. Besides, easy to use as immersion type and non poisonous so waste water
treatment very simple.

Operating condition - RIP MASTER NRP-10 100ml/l, Sulfuric Acid(95%) 100ml/l, Hydrogen Per
oxide(35%) 100ml/l, R.T. -50ーC.

RIP MASTER NRP-20

A stripper agent used for electroless nickel plating on ferrous metals. Can be used at
comparatively low temperature(over 70ーC) and fast stripping rate without defecting
the base metal. Also, stable solution so do not decompose easily and since non poisonous
waste water treatment very simple.

Operating condition - RIP MASTER NRP-20A 100ml/l, RIP MASTER NRP-20B 80-100g/l, Caustic
soda 40g/l.

RIP MASTER NRP-100

Non-cyanide stripping agent for copper, nickel plating on steel base surface.

RIP MASTER NRP-01

Stripping agent for electroless nickel plating on copper and copper alloy base surface.
HIgh speed stripper and do not contain toxic such as cyanide.

RIP MASTER ER-V8

A non cyanide electro type stripping agent to remove plating on stainless steel jig. Have
long life and fast stripping rate so very economical. Best suited for automatic plating line.

Operating condition - Dilute MASTER ER-V8 1-2 water, 10-50ーC, 5-20a/dm2.

RIP MASTER HANDA

Stripper agent for Solder ferrous metals and copper or copper alloy.

Operating condition - on ferrous metals RIP MASTER HANDA No.1 50g/l, Caustic soda 100g/l,
on copper or copper alloy. 1RIP MASTER HANDA No.1 50g/l, Nitric Acid(62-68%) 100-150ml/l
2 RIP MASTER No.2 200ml/l ,Sulfuric Acid(95%) 100ml/l, St Additive 10ml/l.

RIP MASTER ER-V9

A electro type stripping agent to remove copper from through hole plating jig made by
stainless steel. Fast stripping time and since dissolved copper deposit to cathode which
keep solution in good stripping condition so long life use.

Operating condition - RIP MASTER ER-V9 1-2 WATER, ROOM TEMPERATURE, 5-20 A/dm2.

PRETREATMENT CHEMICAL FOR ALUMINIUM & ALUMINIUM ALLOY(MAGNESIUM) BACK

SUPER ZINCATE PROCESS (SZ PROCESS)

Most effective non cyanide pretreatment process for plating on aluminium and aluminium alloy.
Simple operation and treatment process so can obtain good plating adhesion. This process
contain SZ Cleaner, SZ Etchant, SZ Solution and SZ2 Solution. Moreover SZ NN Solution
available for electroless nickel plating.

ALMINIUM SEALING

DAICASEAL NI

Alminium materials' color (daying) sealing.

PRETREATMENT CHEMICAL FOR MAGNESIUM & MAGNESIUM ALLOY

MAGIC PROCESS

Non chromate magnesium chemical conversion without using any metals for suface treatment
of Note Book type personal computers' cover and casing of handy phones.

SUPER MAGNE PROCESS

Most advanced pretreatment method for magnesium and magnesium alloy.
This process contain Mg-Cleaner,Mg-Etchant,Mg-Activation,Mg-Neutralization,Mg-displacement.

IMPURITY REMOVER

NICKERON - NICKERON-G

kizai's original product to remove metal impurities(copper, zinc, ferrous metals, lead, etc.)
in nickel plating solution. NICKRON is in powdered form and NICKERON-G in pellet form. In
case if NICKERON-G put pebble in bag leave in solution so filteration not necessary. Easier
to use but NICKERON in powdered form is more effective of two.

DRYING AGENT

I.D.R.

Remove water from plated surface sametime dry without leaving water strain. Also, have
rust preventive effect.

SUPERCLEEN 100

Remove water from plated surface by chrome or nickel without or stain.

Operating condition - 10-75ml/l, 50-70ーC.


FILTERS AND CARTRIDGE BACK

STANDARD TYPE FILTERS AND K.K. FILTERS

CARTRIDGE TYPE

MOTOR (PUMP) TANK CAPACITY
K-05 100V 20W 100L
K-1 100V 40W 300L
M-3 100V/200V 150/180W 500L
M-4 100V/200V 150/180W 900L
M-6 200V 265/260W 1,000L
M-8 200V 260W 1,200
WA-103M 200V 0.4kW 2,000L
WA154M 200V 0.75kW 3,000L
WA-245M 200V 1.5kW 5,000L
WA-363M 200V 2.2kW 6,000L
WAB-7211 200V 11kW 20,000L

MULTIPURPOSE/OIL & ORGANIC SUBSTANCE REMOVING(O.R.F.)

Use special carbon filter attachment for efficient filtration.
two double filters could be used easy maintenance.
New compact design and light weight.

MOTOR (PUMP) TANK CAPACITY
ORF-3P 1100/200V 150/180W 300L
ORF-6P 200V 265/260W 600L
ORF-10P 200V 0.4kW 1,600L
ORF-15P 200V 0.75kW 2,000L
ORF-24P 200V 1.5kW 3,500L
ORF-36P 200V 2.2kW 4,000L

SPECIAL ATTACHMENTS

CARTRIDGE JUST --- They are developed by KIZAI long ago for life easy handling cartridge for filters.
CARBON JUST --- Carbon type cartridge for filtration nickel plating.
JUST C --- Carbon type cartridge for filtration copper sulfate.
NICKERBON ORF --- Carbon for plating.
NICKERBON P --- Packed by special cloth for protecting carbon inside.